Everlastic® EVA-200G
Click Here
for Tech Data Sheet
 | Description
Cross Linked, Closed Cell, Ethylene/Vinyl/Acetate
Foam
|
|
 |
 |
| Features
Lightweight, Flexible, Resilient, Non-Absorbent
Foam. Resistant to heat, ultraviolet and many chemicals.
|
|
|
Applications
As hot or cold applied sealant backup, to fill
vertical and horizontal joints, acoustical partition closures, corrugated deck closures
and many other uses
Click Here for Application
Examples
|
| Typical Physical Properties
| Property |
Typical Value |
Test Method |
| Color (Standard) |
Gray |
|
| Density (lbs./cu.ft.) |
2.3 ± 0.5 |
ASTM D 3575-91 |
| Compression/Deflection (psi required to compress
25%) |
5 ± 2 |
ASTM D 1056-91 |
| Compression and Recovery
@ 50% |
14.5 psi (10 psi Min. to 25 psi Max.)
99% |
ASTM D 1752-84 Modified (see note 1) |
| Extrusion @ 50% |
0.10 inch |
(see note 2) |
| Ultimate Tensile Strength |
50 psi |
ASTM D 3575-91 |
| Water Absorption |
<5%(Max. Gain by Weight) |
ASTM D1056-91 |
| Odor |
No Objectionable Odor |
|
| K Factor |
0.25 |
|
| Service Temperature Low
High Continuous
High Intermittent |
-70°F
160°F
180°F |
ASTM D 746 |
| Flame Resistance |
Pass |
MVSS-302 |
| Accelerated Aging 7 Day 158°F Flexibility180° Bend
Without Cracking |
Pass |
|
| Appearance Change |
None |
|
| Change in Compression/Deflection |
±30 |
|
| 1.) *After removal of
load, material shall recover to 95% of original thickness within 24 hours* 2.) *When compressed to 50% of material thickness with three
sides restrained, the unrestrained edge shall not extrude more than 0.25 inches.* |
| Generally Resistant to,
Acids, Alkalis, Gasoline & Oil, Aromatic Hydrocarbons, Ketones, Oxidation and Ozone |
|
|