Rubber waterstops provide superior performance in withstanding shear movements and to resist hydrostatic pressure.
The product will elongate four times its original size and continue to near original shape after repeated movement. Rubber waterstops have a very low compression set and perform well at low temperatures.
The Williams System features sleeve-type fittings that provide fast positive splicing and precise waterstop alignment. Fittings are manufactured from the same elastomers/polymers as the waterstop.
|Physical Property||ASTM test Method||“Williams Spec. 2010 Hi-Tensile (SBR) Styrene Butadiene”||“Williams Specification 1025 Hi-Tensile Neoprene”|
|Tensile strength, min (PSI)||ASTM D412||2500*||2500*|
|Ultimate Elongation, Min (%)||ASTM D412||450||450|
|Hardness, Shore A durometer||ASTM D2240||65 +/- 5%||65 +/- 5%|
|Tensile Stress min PSI to produce 300% elongation||ASTM D412||1150||1150|
|Water Absorption, max % by weight after
immersion 7 days at 73.4 degrees F +/- 2 F
|Compression Set, Max % after 22 hours at 158 degrees F||ASTM D395
|Tensile Strength after aging, Min % of original
after 7 days in air at 158 degrees +/- 2 degrees F, and 300 PSI
|Specific Gravity||ASTM D1817||1.17 +/- .03||1.17 +/- .03|
|Ozone cracking resistance after 20% elongation for 7 days 0.5 p/m at 38 degrees C (neoprene 3 p/m)||ASTM D1149||No cracks||No cracks|
|Tensile set, % max after 200% elongation for 10 min at
23 degrees +/- 1 degree C